A Non-Precious Metal Promoting the Synthesis of 5-Hydroxymethylfurfural

Titanium dioxide-supported non-precious metal oxygen reduction electrocatalysts

1. Materials synthesis and characterization Catalyst synthesis: Commercially available TiO 2 , with the particle size ranging from 50 to 150 nm and in the B.E.T. surface area from 50 to 100 m 2 /g, was first treated in 0.5 M HCl solution for 24 hours to remove impurities. In a typical approach to the synthesis of the PANI-Fe-TiO 2 catalyst, 2.0 mL aniline was first dispersed in 0.5 M HCl soluti...

Titanium dioxide-supported non-precious metal oxygen reduction electrocatalyst.

A new non-precious metal oxygen reduction catalyst was developed via heat treatment of in situ polymerized polyaniline onto TiO(2) particles in the presence of Fe species. The TiO(2) provides for improved performance relative to a carbon black-based catalyst and, at a high catalyst loading, allows for reducing the performance gap between non-precious-metal catalyst and Pt/C to ca. 20 mV in RDE ...

Water durability of resin bond to precious metal alloys using adhesive resins containing adhesion promoting monomers.

Adhesive resins for precious metals were prepared by adding an adhesion promoting monomer to MMA-PMMA/TBBO resin. Precious metal alloys bonded by the adhesive resin were thermocycled 0, 1,000, 2,000, or 4,000 times in water between 4 and 60 degrees C, and tensile bond strengths were measured. Debonded metal surfaces after the tensile test were analyzed based on an area of cohesive failure. Thre...

a corpus-based study of the frequency of personal pronouns in translated and comparable non-translated persian texts

چکیده ندارد.

Investigations into the Direct Synthesis of Hydrogen Peroxide and CO Oxidation Using Precious Metal Catalysts