A Micromechanics Based Numerical Investigation of Dual Phase Steels
نویسندگان
چکیده
منابع مشابه
High Temperature Behavior of Dual Phase Steels
Dual phase steels with different martensite volume fraction and morphology were tensile tested at a temperature range of 25 to 5500C. Stress-strain curves of all steels showed serration flow at temperatures of 250 and 3500C, and smooth flow at the other temperatures. Both yield and ultimate tensile strengths increased with increasing testing temperature up to about 450<sup...
متن کاملUltra-Fine Grained Dual-Phase Steels
This paper provides an overview on obtaining low-carbon ultra-fine grained dual-phase steels through rapid intercritical annealing of cold-rolled sheet as improved materials for automotive applications. A laboratory processing route was designed that involves cold-rolling of a tempered martensite structure followed by a second tempering step to produce a fine grained aggregate of ferrite and ca...
متن کاملhigh temperature behavior of dual phase steels
dual phase steels with different martensite volume fraction and morphology were tensile tested at a temperature range of 25 to 5500c. stress-strain curves of all steels showed serration flow at temperatures of 250 and 3500c, and smooth flow at the other temperatures. both yield and ultimate tensile strengths increased with increasing testing temperature up to about 4500c and then decreased at h...
متن کاملultra-fine grained dual-phase steels
this paper provides an overview on obtaining low-carbon ultra-fine grained dual-phase steels through rapid intercritical annealing of cold-rolled sheet as improved materials for automotive applications. a laboratory processing route was designed that involves cold-rolling of a tempered martensite structure followed by a second tempering step to produce a fine grained aggregate of ferrite and ca...
متن کاملThe Effect of Ferrite Grain Size on the Fatigue Behavior of Ferrite-martensite Dual-phase Steels
The effect of ferrite grain size on the fatigue and tensile properties of dual phase steels with a 0.25 volume fraction of martensite (Vm) under different heat treatments was investigated. The heat treatments were homogenized at 1200 oC along with several subsequent normalizations at 910 oC, resulting in different microstructures and mechanical properties. After heat treatment, the obtained ste...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Structural Integrity
سال: 2019
ISSN: 2452-3216
DOI: 10.1016/j.prostr.2019.12.087