7xxx aluminum alloys; strengthening mechanisms and heat treatment: a review
نویسندگان
چکیده
منابع مشابه
Strengthening Mechanisms in the Aged 2024 and 7075 Aluminium Alloys
Aluminum 2024 and 7075 alloys which are widely used in aerospace and marine applications were chosen to investigate their strengthening mechanisms. Using differential thermal analysis (DIA), metallography and tension tests, the best solutionizing conditions were determined to be 500±5°C and 2 hours for 2024 and 480?±5°C and 1 hour for 7075 alloy. Aging was performed in the range of 100 to 200°C...
متن کاملHeat Treatment of Dental Alloys: A Review
Metallic materials have widespread use in dentistry for clinical treatment and restoration of teeth. Major areas of usage are: (1) restorative dentistry and prosthodontics (dental amalgam and gold alloy restorations for single teeth, metallic restorations for multiple teeth, including metal-ceramic restorations, removable partial denture frameworks, and dental implants), (2) orthodontics (wires...
متن کاملPorosity Development during Heat Treatment of Aluminum-lithium Alloys
The development of a sub-surface layer of porosity during heat treatment has been studied in a variety of A1-Li alloys. Pure binary A1-Li alloys and three commercial materials were heat treated in air, vacuum and hydrogen for various lengths of time. Subsequent metallographic sectioning and polishing revealed the presence of a band of pores in the near-surface region extending approximately 300...
متن کاملQuench Rate Effects on the Natural Aging Behavior of 7xxx Al-mg-zn-cu Aluminum Alloys
The effect of quench rate on the natural aging behavior was examined using microhardness, conductivity and the differential scanning calorimeter. The data indicated that GPZ formed during extended natural aging of 7075, while extended aging of 7050 resulted in the precipitation of η’. Introduction The aluminum alloy system Al-Zn-Mg-Cu is the mainstay of aluminum alloys used in the aerospace ind...
متن کاملEffect of Post-weld Heat Treatment on Joint Properties of Dissimilar Friction Stir Welded AA2024 and AA7075 Aluminum Alloys
In present study, the effect of heat treatment after friction stir welding dissimilar welds T6-7075 and T4-2024 aluminum alloys were investigated. Friction stir welding was performed at a constant rotation speed of 1140 rpm and welding speed 32 mm/min. After welding samples are taken under various heat treatment processes at different aging temperature and time period. Microstructural observati...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Material Science & Engineering International Journal
سال: 2018
ISSN: 2574-9927
DOI: 10.15406/mseij.2018.02.00034