2D Surface Structures in Small Zeolite MFI Crystals

2D Zeolite Coatings: Langmuir-Schaefer Deposition of 3 nm Thick MFI Zeolite Nanosheets.

Stable suspensions of zeolite nanosheets (3 nm thick MFI layers) were prepared in ethanol following acid treatment, which partially removed the associated organic structure-directing agent. Nanosheets from these suspensions could then be dispersed at the air-water interface and transferred to silicon wafers using Langmuir-Schaefer deposition. Using layer-by-layer deposition, control on coating ...

Crystallographic Structure Determination of MFI-Zeolite Nanosheets

Ultrathin MFI-zeolite nanosheets can be packed on porous supports to create molecular sieve membranes. The nanosheets on porous support reduce morphological damage seen in regular MFIzeolite crystals [1]. MFI-zeolite belongs to pentasil family of zeolites where the periodic building unit (PerBU) is composed of 12 interconnected SiO4 tetrahedral (T12) units of 41m2 (D2d) symmetry [2]. Rotation o...

Microwave fabrication of MFI zeolite crystals with a fibrous morphology and their applications.

Gas Diffusion in Polycrystalline MFI-type Zeolite Membranes

1. Introduction 1. Introduction Information on mass transport in polycrystalline zeolite membranes is necessary for a theoretical estimation of the membrane performances. Zeolite membranes are usually prepared as thin layer of an assembly of small zeolite crystals including many intercrystalline regions. Thus, the intercrystal region would influence their individual diffusion properties, which ...

Tubular MFI Zeolite Membranes Made by In-Situ Crystallization

Polycrystalline MFI zeolite membranes were prepared on α-alumina tubular support by hydrothermal treatments at 413 K. The synthesized zeolite membranes were characterized by XRD, SEM and single gas permeation. The influence of hydrothermal treatment steps and the calcination time on the zeolite layer formation were investigated. MFI zeolite membrane prepared by four subsequent hydrothermal ...